 abstract={The paper presents results of compressive strength investigations of EN AC-44200 based aluminum alloy composite materials reinforced with aluminum oxide particles at ambient and at temperatures of 100, 200 and 250C. They were manufactured by squeeze casting of the porous preforms made of α-Al2O3 particles with liquid aluminum alloy EN AC-44200. The composite materials were reinforced with preforms characterized by the porosities of 90, 80, 70 and 60 vol. %, thus the alumina content in the composite materials was 10, 20, 30 and 40 vol.%. The results of the compressive strength of manufactured materials were presented and basing on the microscopic observations the effect of the volume content of strengthening alumina particles on the cracking mechanisms during compression at indicated temperatures were shown and discussed. The highest compressive strength of 470 MPa at ambient temperature showed composite materials strengthened with 40 vol.% of α-Al2O3 particles.},
 type={Artykuły / Articles},
 title={Compressive Strength of EN AC-44200 Based Composite Materials Strengthened with α-Al2O3 Particles},
 URL={http://ochroma.man.poznan.pl/Content/102006/PDF/afe-2017-0049.pdf},
 doi={10.1515/afe-2017-0049},
 keywords={compressive strength, Composite materials, Aluminum oxide particles},
}