 abstract={Describes how to obtain a soluble sodium silicate with a density of 1.40 g/cm3, 1.45 g/cm3, 1.50 g/cm3, and silica module M = 2.1 obtained from the silica- sodium glass with module M = 3.3 and M = 2.1. Residual (final) strength of molding samples made with these binders, were determined at temperatures corresponding to the characteristic temperatures of phase and temperature transitions of silica gel. Indicated the type of soluble sodium silicate capable of obtain the smallest value of the final strength of molding sand in the specified range of temperatures.},
 type={Artykuły / Articles},
 title={The Influence of Silica Module of the Soluble Sodium Silicate Hardened by Ester on the Residual Strenght of Molding Sand},
 URL={http://ochroma.man.poznan.pl/Content/87319/PDF/25_paper.pdf},
 doi={10.2478/afe-2013-0025},
 keywords={Soluble sodium silicate, Silica gel, Residual strength},
}